方管在制造過程中會出顯不同的問題，采用不同方法制造出的方管出現(xiàn)的問題也是不同的，我們會根據(jù)出現(xiàn)的問題，采用合適的方法進行處理，以確保方管可以正常的使用，下面主要為大家介紹一下方管熱處理后出現(xiàn)的質(zhì)量缺陷。 方管經(jīng)熱處理后常見的質(zhì)量缺陷有：淬火顯微組織過熱、欠熱、淬火裂紋、硬度不夠、熱處理變形、表面脫碳、軟點等，’它們對方管的使用壽命和精度具有重要的影響，分析芄產(chǎn)生的原因，對于指導(dǎo)熱處理過程和預(yù)防有重要的作用。

Square pipe will show different problems in the manufacturing process, and the problems arising from different manufacturing methods are also different. We will adopt appropriate methods to deal with the problems, so as to ensure the normal use of Square pipe. The following is mainly about the quality defects of Square pipe after heat treatment. Common quality defects of square pipe after heat treatment are: quenching microstructures overheating, underheating, quenching cracks, insufficient hardness, heat treatment deformation, surface decarbonization, soft point, etc.'They have important influence on the service life and accuracy of square pipe. Analyzing the causes of the formation of Juan has an important role in guiding the heat treatment process and prevention.

1、方管過熱：

1. Square tube overheating:

從方管粗糙口上可觀察到淬火后的顯微組織過熱情況。但i 要確切判斷其過熱的程度，必須觀察顯微組織。如果GCrl5鋼的淬火組織中出現(xiàn)粗針狀馬氏體，則為淬火過熱組織。形成原因可是淬火加熱溫度過高或加熱保溫時間太長造成的全面過熱;也可肖巨是因原始組織帶狀碳化物嚴重，在兩帶之間的低碳區(qū)形成局部馬氏體針狀粗大，造成的局部過熱。過熱組織中殘留奧氏體增多，尺寸穩(wěn)定性下降。由于淬火組織過熱，鋼的晶體粗大·會導(dǎo)致方管的核J 性下降·抗沖擊性能降低，方管的壽命也降低。過熱嚴重甚至?xí)斐纱慊鹆鸭y。

Overheating of quenched microstructures can be observed from the rough mouth of square tubes. However, in order to determine the degree of overheating, we must observe the microstructures. If coarse acicular martensite appears in the quenched structure of GCrl5 steel, it is quenched superheated structure. The reason is that the quenching heating temperature is too high or the heating holding time is too long, which results in the overall overheating. It can also be said that Xiao Ju is the local overheating caused by the formation of local martensite needle-like coarseness in the low-carbon zone between the two zones due to the serious ribbon carbides in the original structure. The retained austenite in the superheated structure increases and the dimensional stability decreases. Due to the overheating of quenched structure, the coarse crystal of steel will lead to the decrease of core J property, impact resistance and service life of square tube. The severe overheating may even cause quenching cracks. 2、方管熱處理變形：

2. Heat treatment deformation of square pipe:

方管在熱處理時，存在有熱應(yīng)力和組織應(yīng)力，這種內(nèi)應(yīng)力能相互疊加或部分抵消，是復(fù)雜多變的，因為它能隨著加熱溫度、加熱速度、冷卻方式、冷卻速度、零件形狀和大小、裝爐的方式的變化而變化，故其熱處理變形是難免的。認識和掌握它的變化規(guī)律可以使軸承零件的變形(如合金管的橢圓、尺寸脹大等)置于可控的范圍，有利于生產(chǎn)的正常進行。當(dāng)然在熱處理過程中的機械碰撞也會使零件產(chǎn)生變形，但這種變形是可以通過改進操作等來加以減少和避免的。

There are thermal stress and organizational stress in square tube during heat treatment. The internal stress can be superimposed or partially offset each other, which is complex and changeable. Because it can change with the change of heating temperature, heating speed, cooling mode, cooling speed, shape and size of parts, and charging mode, the heat treatment deformation of square tube is unavoidable. Understanding and mastering its changing law can make the deformation of bearing parts (such as the ellipse of alloy tube, size expansion, etc.) in a controllable range, which is conducive to the normal production. Of course, mechanical collision in the heat treatment process will also cause deformation of parts, but this deformation can be reduced and avoided by improving operation.

3、方管軟點：

3. Soft spot of square pipe:

多半是由于加熱不足、冷卻不良或淬火操作不當(dāng)?shù)仍蛟斐傻姆焦鼙砻婢植坑捕炔粔虻默F(xiàn)象稱為淬火軟點。它像表面脫碳一樣可以造成表面耐磨性和疲勞強度的嚴重下降，使用過程中將造成局部劇烈磨損或失效。

The phenomenon that the local hardness of square tube surface is not enough due to insufficient heating, poor cooling or improper quenching operation is called quenching soft point. Like surface decarbonization, it can cause serious decrease in wear resistance and fatigue strength of the surface, which will cause severe local wear or failure during use.

方管在熱處理時出現(xiàn)的問題，我們會對方管進行深刻的研究，把方管的的質(zhì)量保證可以合理的利用。我們把方管制作成型后，會對方管進行全方位的檢測，讓方管的質(zhì)量得以保證，在實際運用中讓顧客滿意。

We will make a deep study of the problems that occur in the heat treatment of square pipes, so that the quality assurance of square pipes can be reasonably utilized. After forming the square tube, we will carry out all-round inspection of the square tube, so that the quality of the square tube can be guaranteed and the customers can be satisfied in practical application.